| 廠家(產(chǎn)地) | 沙特巴塞爾 |
|---|---|
| 牌號 | HP500N |
| 加工級別 | 注塑級 |
| 特性級別 | 高剛性,高流動 |
| 用途級別 | 通用級 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標準料 |
| Typical Properties | Method | Value | Unit |
| Physical | |||
| Density | ISO 1183 | 0.9 | g/cm? |
| Melt flow rate (MFR) (230°C/2.16kg) | ISO 1133 | 12 | g/10 min |
| Melt volume flow rate (230°C/2.16kg) | ISO 1133 | 16 | cm?/10min |
| Mechanical | |||
| Tensile Modulus | ISO 527-1, -2 | 1550 | MPa |
| Tensile Stress at Yield | ISO 527-1, -2 | 35 | MPa |
| Tensile Strain at Break | ISO 527-1, -2 | >50 | % |
| Tensile Strain at Yield | ISO 527-1, -2 | 10 | % |
| Impact | |||
| Charpy unnotched impact strength | ISO 179 | ||
| (23 °C, Type 1, Edgewise) | 110 | kJ/m? | |
| (0 °C, Type 1, Edgewise) | 30 | kJ/m? | |
| Charpy notched impact strength (23 °C, Type 1, Edgewise, Notch A) | ISO 179 | 3 | kJ/m? |
| Thermal | |||
| Heat deflection temperature B (0.45 MPa) Unannealed | ISO 75B-1, -2 | 95 | °C |
| Vicat softening temperature A/50 | ISO 306 | 153 | °C |
| Vicat softening temperature B/50 | ISO 306 | 85 | °C |
聚丙烯，是由丙烯聚合而制得的一種熱塑性樹脂。按甲基排列位置分為等規(guī)聚丙烯（isotactic polyprolene）、無規(guī)聚丙（atacticpolypropylene）和間規(guī)聚丙烯（syndiotactic polypropylene）三種。甲基排列在分子主鏈的同一側(cè)稱等規(guī)聚丙烯，若甲基無秩序的排列在分子主鏈的兩側(cè)稱無規(guī)聚丙烯，當甲基交替排列在分子主鏈的兩側(cè)稱間規(guī)聚丙烯。一般工業(yè)生產(chǎn)的聚丙烯樹脂中，等規(guī)結(jié)構(gòu)含量約為95%，其余為無規(guī)或間規(guī)聚丙烯。
工業(yè)產(chǎn)品以等規(guī)物為主要成分。聚丙烯也包括丙烯與少量乙烯的共聚物在內(nèi)。通常為半透明無色固體，無臭無毒。由于結(jié)構(gòu)規(guī)整而高度結(jié)晶化，故熔點可高達167℃。耐熱、耐腐蝕，制品可用蒸汽消毒是其突出優(yōu)點。密度小，是**的通用塑料。缺點是耐低溫沖擊性差，較易老化，但可分別通過改性予以克服。
共聚物型的PP材料有較低的熱變形溫度（100℃）、低透明度、低光澤度、低剛性，但是有更強的抗沖擊強度，PP的沖擊強度隨著乙烯含量的增加而增大。PP的維卡軟化溫度為150℃。由于結(jié)晶度較高，這種材料的表面剛度和抗劃痕特性很好。PP不存在環(huán)境應力開裂問題。
PP的熔體質(zhì)量流動速率（MFR）通常在1~100。低MFR的PP材料抗沖擊特性較好但延展強度較低。對于相同MFR的材料，共聚型的抗沖強度比均聚型的要高。由于結(jié)晶，PP的收縮率相當高，一般為1.6~2.0%。